- YUHONG brand goods have been already exported to more than 85 countries With more than 35 years' experience, because of strict quality control policy, excellent sales service, delivery on time. YUHONG won more and more new clients and got more and more repeat orders from old clients, in YUHONG People's mind: Quality is First Important!
ASTM A312 TP316L (UNS S31603) Stainless Steel Seamless Pipe for Petrochemical
ASTM A312 TP316L (UNS S31603) is a low-carbon austenitic stainless steel seamless pipe designed for high corrosion resistance and high-temperature service in petrochemical, chemical processing, oil & gas, and other demanding industries. It offers superior pitting and crevice corrosion resistance compared to standard 316 stainless steel due to its reduced carbon content (≤0.03%), minimizing carbide precipitation during welding and thermal cycling.
1.Chemical & Mechanical Properties
| ASTM A312 TP316L Chemical Composition (%) |
| C | Mn | P | S | Si | Cr | Ni | Mo | N |
| ≤0.03% | ≤2.00% | ≤0.045% | ≤0.030% | ≤0.75% | 16.0%~18.0% | 10.0%~14.0% | 2.00%~3.00% | ≤0.1% |
Mechanical Properties
| Property | Standard Value (Annealed) |
| Tensile Strength | ≥485 MPa |
| Yield Strength | ≥170 MPa |
| Elongation | ≥40% |
| Hardness | ≤217 HB (Brinell) |
2. Key Adventages
- Superior Corrosion Resistance
Resistant to chlorides & acids: Molybdenum (2-3%) enhances resistance to chlorides, seawater, sulfuric/phosphoric acids, ideal for marine/chemical industries.
Low-carbon anti-sensitization: Carbon ≤0.03% prevents intergranular corrosion during welding/thermal cycles.
-
High-Temperature & Pressure Performance
High-temperature stability: Continuous service up to 925°C (intermittent 870°C), suitable for heat exchangers/boilers.
Seamless design: No welded joints, higher pressure tolerance (ASME B31.3 compliant).
-
Excellent Weldability & Fabrication
No post-weld treatment: Low carbon minimizes carbide precipitation, enabling direct welding.
Easy fabrication: Austenitic structure allows cold bending/flaring.
3. Key Applications
Refinery piping systems: Transporting crude oil, refined products, and corrosive media (e.g., sulfides, acidic gases).
Heat exchangers & reactors: High-temperature/pressure heat transfer components.
Catalytic cracking units: Resistant to high-temperature sulfur corrosion and hydrogen embrittlement.
Acid/alkali transfer pipelines: For sulfuric, hydrochloric, and phosphoric acids.
Solvent production equipment: Resistant to organic solvents (e.g., methanol, ethanol).
Polymer production: Resists chloride-induced stress corrosion cracking (SCC).
Subsea pipelines: Resistant to seawater corrosion and microbiologically influenced corrosion (MIC).
LNG equipment: Maintains toughness in cryogenic conditions (-196°C).
Offshore platform components: Load-bearing parts in high-salinity environments.
Sanitary piping: Contamination-free transfer of high-purity fluids (FDA compliant).
Bioreactors: 316L material withstands clean-in-place/sterilize-in-place (CIP/SIP).
| Comparison Item | TP316L (UNS S31603) | TP316 (UNS S31600) |
| Carbon Content | ≤0.03% (Ultra-low carbon, superior intergranular corrosion resistance after welding) | ≤0.08% (Standard carbon content, may sensitize after welding/high temperatures) |
| Corrosion Resistance | Excellent (Low carbon minimizes carbide precipitation, superior pitting/crevice corrosion resistance) | Good (But may lose corrosion resistance due to carbide precipitation in harsh conditions) |
| Weldability | No post-weld annealing required (Cost-effective for welded structures) | May require post-weld heat treatment (To prevent intergranular corrosion) |
| High-Temp Performance | Suitable for continuous service up to 925°C (Reduced chromium carbide formation) | Suitable for ≤870°C (Long-term high temp may cause weakening) |
| Mechanical Strength | Tensile: ≥485 MPa, Yield: ≥170 MPa (Slightly lower than TP316) | Tensile: ≥515 MPa, Yield: ≥205 MPa (Higher strength) |
| Primary Applications | Chemical/offshore/nuclear (Harsh corrosive environments) | General industry/food processing (Moderate conditions) |
| Cost | Slightly higher (Due to low-carbon control process) | Slightly more economical (Standard composition) |